Appearance: milky white with blue light

Solid content: 48 ± 1%

Cross linking mode: double cross linking

Polymeric structure: core shell

Fluorine content: ≥ 10% (based on solids)

Density: 1.05~1.08 g/ml (25C °)

Brinell viscosity: 1000 ~ 3500mpa • s

Theoretical glass transition temperature: 30 ℃

Dosage of film forming aids: 8% (at 5 ℃, the amount of film forming aids required for varnish film forming)

P H value: 7 ~ 9

Ion attribute: anionic

*It only represents typical results and is not considered as a specification, subject to specific COA.

Product Description

There are three national standards for waterborne fluorocarbon: PVDF, FEVE, fluoroacrylic acid. This product belongs to fluoroacrylic acid

Product features:

1.Fluorine containing acrylic acid lotion, with good emulsion paint formula applicability and wide selectivity of additives;

2. The double self crosslinking fluorocarbon lotion was prepared by core-shell lotion polymerization with soft core and hard shell particles;

3. Super long weather resistance, anti contamination, no yellowing;

4. Alkali resistance, acid rain resistance and salt fog resistance;

5. Excellent water resistance.

First aid:

Eyes: If the paint splashes into the eyes, wash them with water immediately and ask a doctor for treatment.

Skin: If the skin is stained with paint, wash it with soap and water or use appropriate industrial cleaning agent.

Inhalation or ingestion: If you accidentally swallow lotion, please ask a doctor for treatment immediately.

Storage method:

The storage environment should be dry, cool, well ventilated, and avoid low temperature freezing and high temperature; The packaging container must be kept closed.

The storage period is 12 months. After that, it shall be used after passing the inspection.


50kg/plastic bucket, 1000kg/plastic bucket.


The use conditions of customers are beyond our control, and we cannot guarantee that all recommendations and suggestions are appropriate. The relevant technical specifications will change, so no further explanation will be given.